Maintenance of hot dip galvanizing line equipment
The hot-dip galvanizing process consists of three steps: surface preparation, galvanizing, and inspection.
Surface Preparation: For high quality hot-dip galvanizing, steel must be properly prepared prior to being immersed in a bath of molten zinc. During the surface preparation stage, material going through degreasing/caustic cleaning, pickling, and fluxing.
Degreasing/Caustic Cleaning: A hot alkali solution, mild acidic bath, or biological cleaning bath removes contaminants from the steel such as dirt, grease and oil.
Pickling: To remove mill scale and iron oxides, the steel goes through a diluted solution of heated sulfuric acid or ambient hydrochloric acid.
Fluxing: Through the final surface preparation step, any remaining oxides are removed in a zinc ammonium chloride solution and a protective layer is deposited on the steel to prevent any further oxides from forming prior to galvanizing.
Galvanizing: Following surface preparation, the steel will be immersed in a bath of molten zinc. The zinc kettle contains at least 98% pure zinc and is maintained at a temperature between 815º-850º F (435º-455º C). While steel is immersed in the kettle, the zinc reacts with the iron in the steel to form a series of metallurgically bonded zinc-iron alloy layers with the final top layer 100% zinc.
Inspection: The inspection process of galvanized steel is fairly simple. Zinc will not react with unclean steel, therefore a visual inspection of the product will provide a good assessments of the quality of the coating. Tests for coating thickness and adherence to ASTM standards will also be performed.
To learn more about the galvanizing process, schedule a consultation or seminar with your local facility.
laminated magnet Inconel Wire Alkali-free Fiberglass Filter Mesh For Aluminium Welded Razor Wire Mesh glass blasting media near me stainless steel welded wire mesh Socket Fig Long Life Crucible Clamps Pot Magnet Motor Magnet Galvanized Steel Coils 30LBS RAIL Titanium Perforated Sheet Stainless steel ferrule mesh Metal coil mesh petroleum coke